Feature(may vary by option.)

●【AMI-7000S Anion Exchange Membrane】 Thickness: 0.45 mm 0.025mm Resistance (Q.cm2) 0.5mol /L NaCI: <40 Maximum current (A/m2): <500 Selectivity (%)0.1 mol KCI/kg/0.5 mol KCI/kg: 90 Exchange capacity (meq/g): 1.3 oz 0.1
●【AMI-7000S Anion Exchange Membrane】 Water permeability (ml/hr/ft2) @5psi: <3 Explosion strength (psi): >80 Maximum operating temperature (℃/): 90℃/ 194°F pH range: 1~10
●【AMI-7000S Anion Exchange Membrane】Desalination use: Soak the ionic membrane in 3~5wt%NaCI solution for 24 hours to fully hydrate and expand the interior of the membrane
●【AMI-7000S Anion Exchange Membrane】Electrolytic use: Soak the ionic membrane in the working medium solution or deionized aqueous solution for 24 hours before use
●【AMI-7000S Anion Exchange Membrane】Storage method: After receiving the goods, the diaphragm can be stored in a dry state, stored in a sealed bag at room temperature and low humidity. The used membrane should be washed with clean water and soaked in deionized water for medium and long term storage. The aqueous solution should be replaced regularly every month. The used membrane should not be dried for storage


Description

Thickness: 0.45 mm 0.025mm
Resistance (Q.cm2) 0.5mol /L NaCI: <40
Maximum current (A/m2): <500
Selectivity (%) 0.1mol KCI/kg/ 0.5mol KCI/kg: 90
Exchange capacity (meq/g): 1.3 oz 0.1
Water permeability (ml/hr/ft2) @5psi: <3
Bursting strength (psi): >80
Maximum operating temperature (℃/): 90℃/ 194°F
pH range: 1~10